Blog by Kenneth Lieblich
This is the story of a pipe – possibly damaged beyond reasonable limits – which I really liked and decided (against my better judgement) to revivify. I need to make clear from the outset that this is not a pipe like many you see from Steve, Dal, Paresh, Charles, et al, which begin their restoration as the proverbial sow’s ear and naturally end up as the silk purse. No, this is a pipe that came to me as a damaged ‘beast’ and ended up much improved – but a ‘beast’ it remains. There is damage to the pipe which is, despite my best efforts, a permanent attribute. I leave it to your collective judgement on whether it will ever attain the rank of ‘beauty’.
This pipe came from a lot from Sudbury, Ontario. There were literally no marks of any kind on the stummel, stem, or ferrule. In the absence of a name, Steve and I dubbed it ‘The Sudbury’ and that is the name that stuck. Steve thinks that the Sudbury could be of Italian origin, and I have no reason to question that assessment. So let us pretend that it is an Italian ‘scoop’ pipe that arrived from Northern Ontario. If you have any insight into the pipe’s origin, I would love to hear from you. The photos do not quite convey just how bad this pipe looked when it arrived. The stummel was filthy, scratched, dented, cracked, and burned. The bowl was out-of-round, had lots of lava, cake and burns. The stem was oxidized, calcified, and badly pitted (more about the pitting later). The ferrule was dirty, torn, dented, and cheap-looking – it had obviously been put there to address the cracks in the shank. Where to even begin with this mess?
Well, the start came with removing the sorry-looking ferrule, which, quite frankly, inspired more pathos than confidence. This allowed me to have a good look at the cracks (plural) in the shank. As you can plainly see, the cracks were a mess. I removed what I could of lose debris and glue from these fissures, with the intention of refilling them later.Next was reaming out the bowl. This pipe has quite a wide and curved bowl and it required both the PipNet Reamer and the KleenReem. I took it down to bare briar, as I wanted to ensure there were no hidden flaws in the walls of the bowl. Fortunately, there were none. I then proceeded to clean out the insides of the shank with Q-tips, pipe cleaners, and isopropyl alcohol. This is a pipe that really could have used the services of a retort system, but – alas – I do not have one. If anyone has a spare, please let me know. The fellow on eBay who sells them is out of commission for a while. A quick wipe of the outside revealed that there is really some beautiful wood grain in this pipe.A de-ghosting session seemed in order to rid this pipe of the foul smells of the past. This de-ghosting consisted of thrusting cotton balls in the bowl and the shank, and saturating them with 99% isopropyl alcohol. This caused the oils, tars and smells to leech out into the cotton. Finally, a relatively clean and fresh-smelling bowl emerged.While all of that was going on, I cleaned out the insides of the stem with pipe cleaners and isopropyl alcohol. Then the stem went for an overnight soak in the Before & After Hard Rubber Deoxidizer. I knew the stem was going to require a lot of work, but even I did not know what I was getting myself into. The following day, I cleaned all of the de-oxidizing goop (technical term) off with alcohol, pipe cleaners, et cetera. The oxidation had migrated to the surface and would be fairly straightforward to remove.Back to the stummel – and this required addressing two key issues: the badly out-of-round bowl opening and the cracks in the shank that needed to be re-mended. In order to address the out-of-round issue, I took a solid wooden sphere, wrapped sandpaper around it, and sanded thoroughly – until such time as the bowl was returned to round. This process was not difficult, but it was time consuming. I had to ensure that I was sanding down the correct parts that needed it and that I was not removing too much. In the end, I think I got the balance just right.Meanwhile, I had to figure out what could be done with the very noticeable cracks in the shank. The previous ferrule had done a passable job of hiding them, but that ferrule was a non-starter. It was ugly and trashed. Anyway, an application of briar dust and cyanoacrylate adhesive seemed to be the way to go in addressing the cracks. I also had to concede that, no matter what, the cracks were always going to be a visible part of this pipe from now on. There was just no way around it. I sanded down the repairs and left them for a bit later.There was a small burn on the underside of the stummel that also needed to be addressed. I took some oxalic acid on a Q-tip and rubbed and rubbed. The burn did improve but never fully disappeared. I took solace from the fact that the burn was very superficial and did not affect the integrity of the wood at all.After this, I used all nine Micromesh pads (1,500 through 12,000 grit) to sand everything smooth. A light application of Before & After Restoration Balm brought out the best in the stummel’s grain.Steve was kind enough to find me a new ferrule that we could bend to correctly fit the oval shank. This was not as easy as it sounds because the shank’s width tapered away from the end. I used a combination of heat, glue and elbow grease to fit it. I then used metal sandpaper to even out the edge. A quick polish with my cloth made it look pretty good.Now on too the stem. Oh boy – this was a struggle. All the usual things were fine. As I mentioned, the deoxidizing went well; the cleaning of the internals went well; the sanding of the stem with the Micromesh pads went well; the buffing and polishing went well; BUT the pitting was very difficult. In the first place, the pits were all filled with filth and/or oxidation and/or debris from the many years of neglect. In order to dislodge this, I soaked the pitted part of the stem overnight in a lemon-infused, isopropyl alcohol solution. This worked surprisingly well. The debris either dissolved or was easy to scrub out.Now, how to fill these properly so as to create a smooth and (hopefully) invisible repair? Steve assured me that he had successfully filled pits in the past with cyanoacrylate adhesive. Perfect – I set about carefully smearing the adhesive all over the pitting. I left it to set and came back later to sand it down. So far, so good, but some of the pits did not fill (no idea how that happened) and others just looked terrible after sanding. I obviously did something wrong. Steve suggested that we used some black cyanoacrylate adhesive. He very kindly did his own smearing of the black adhesive on my stem. We let it set, did all the right things, and it still looked lousy. I even tried using a black Sharpie to see if that would help – it didn’t. Suffice it to say that I went through this process a total of FOUR times before I had to admit defeat. I will say that the stem looks so much better than when I started, but those pits were *ahem* the pits.I applied more Before & After Restoration Balm, then some wax. I polished it by hand with a microfibre cloth and I was pleased with the results! This pipe was clearly a great beauty on the day it was made. Over the years, abuse, neglect, and the ravages of time turned this charming pipe into a beast. I worked harder on this pipe than I have on any other, but I am proud of it and I am adding it to my collection. I look forward to smoking it for many years to come.
The dimensions of the pipe are as follows: length 164 mm; height 42 mm; bowl diameter 149 × 44 mm; chamber diameter 23 mm. The mass of the pipe is 46 grams. Thank you very much for reading and, as always, I welcome and encourage your comments.